BROCK Material PMC 1706 uretaanikumi-sarja, 2 gallonaa, Shore A60, 1:1 sekoitus, meripihka

For professionals who demand a reliable room-temperature-curing urethane rubber, the BROCK Material PMC 1706 stands out with its balanced 1:1 mix ratio and forgiving 30-minute pot life. This 2-gallon kit delivers a flexible, high-strength material that captures fine detail without the brittleness common in budget alternatives.

Highlights

• Shore A60 hardness: flexible yet tough enough for demanding applications
• Simple 1A:1B mix ratio by weight or volume reduces measuring errors
• 30-minute pot life allows ample working time for complex molds
• Low mixed viscosity (1000 cps) ensures excellent flow into intricate details
• Negligible shrinkage (<0.001 in/in) preserves dimensional accuracy

In daily use

PMC 1706 excels in casting, mold making, and producing industrial parts such as gaskets, seals, and impact pads. Its cured amber color provides a neutral base for pigmentation if desired. The material offers good resistance to many solvents, oils, and fuels, making it suitable for automotive and industrial environments. Demold parts after 16 hours; full properties develop over 7 days. With a maximum operating temperature of 85°C, it handles moderate heat without softening.

Full specifications

• Product Type: Urethane Rubber
• Kit Size: 2 Gallon (approx. 7.57 Liters)
• Shore Hardness: A60
• Mix Ratio (by weight): 1A:1B
• Mix Ratio (by volume): 1A:1B
• Pot Life: 30 minutes
• Cure Time (Demold): 16 hours
• Cure Time (Full): 7 days
• Color (Cured): Amber
• Specific Gravity (Mixed): 1.05 g/cm³
• Tensile Strength: 13.8 MPa (2000 psi)
• Elongation at Break: 450%
• Tear Strength (Die C): 35 kN/m (200 pli)
• Viscosity (Mixed): 1000 cps
• Shrinkage: <0.001 in/in
• Maximum Operating Temperature: 85°C (185°F)
• Processing Method: Room Temperature Cure
• Flexibility: Flexible
• Chemical Resistance: Good against many solvents, oils, and fuels
• Application: Casting, mold making, industrial parts, gaskets, seals, impact pads

Final note

BROCK Material PMC 1706 is a versatile urethane rubber that balances ease of use with professional-grade performance, making it a smart choice for both prototyping and production runs.