ESUN PLA+ 1,75 mm beige 3D-filamentti, 1 kg

ESUN PLA+ in beige is a step above standard PLA, engineered for higher strength and smoother printing. With a tensile strength of 55–65 MPa and elongation at break of 11–20%, it delivers parts that are tougher and more impact-resistant than regular PLA, while retaining the easy printability that makes PLA popular. The beige colour offers a warm, natural tone ideal for prototypes, architectural models, and decorative items.

Highlights

• Enhanced PLA+ formulation for superior strength and durability
• Precision 1.75 mm diameter with ±0.03 mm tolerance
• Low warping and odour for a pleasant printing experience
• Vacuum-sealed with desiccant to maintain filament quality
• Compatible with most FDM 3D printers

In daily use

This filament prints reliably across a wide temperature range. Recommended nozzle temperature is 205–225 °C, and the heated bed can be set from 25–70 °C, giving flexibility for different printer setups. The spool is neatly wound and tangle-free, ensuring consistent extrusion. With a density of 1.24 g/cm³ and a melt flow index of 5–10 g/10min, it flows smoothly for detailed prints. The beige colour hides minor imperfections well and takes paint or post-processing easily if desired.

Full specifications

• Material: PLA+
• Filament diameter: 1.75 mm
• Diameter tolerance: ±0.03 mm
• Colour: Beige
• Net filament weight: 1 kg
• Recommended print temperature: 205–225 °C
• Recommended bed temperature: 25–70 °C
• Density: 1.24 g/cm³
• Tensile strength: 55–65 MPa
• Elongation at break: 11–20%
• Melt flow index: 5–10 g/10min (210°C, 2.16 kg)
• Spool inner diameter: 56 mm
• Spool outer diameter: 200 mm
• Spool width: 64 mm
• Vacuum sealed: Yes, with desiccant
• Compatibility: FDM 3D printers
• Biodegradable: Yes
• Odour: Low
• Warping: Low
• Bubbles: No

Final note

ESUN PLA+ beige is a reliable choice for makers who want stronger prints without compromising on ease of use. Its consistent diameter and low warping make it suitable for both beginners and experienced users.