Polymaker Fiberon PA12-CF10 hiilikuitu nylon filamentti 1,75mm 0,5kg musta FG04001

Engineering-grade materials often force a compromise between strength, stiffness, and ease of printing. The Polymaker Fiberon PA12-CF10 solves this by combining nylon 12 with 10% chopped carbon fiber, delivering exceptional mechanical properties and low warpage for demanding applications.

Who is it for

Professional users and advanced hobbyists who need functional parts that withstand high temperatures and mechanical stress, such as jigs, fixtures, and end-use components.

Main features

• PA12 nylon reinforced with 10% chopped carbon fiber for high strength and stiffness
• Excellent heat resistance with HDT of 150 °C at 0.45 MPa
• Low warpage compared to unfilled nylon, improving print reliability
• 1.75 mm diameter, 0.5 kg spool
• Black color

Specifications

• Material: PA12 with 10% chopped carbon fiber
• Filament diameter: 1.75 mm
• Spool weight: 0.5 kg
• Color: Black
• Recommended nozzle temperature: 280-300 °C
• Recommended bed temperature: 25-50 °C
• Recommended print speed: 30-60 mm/s
• Cooling fan: Off
• Abrasiveness: Highly abrasive (requires hardened nozzle)
• Density: 1.02 g/cm³
• Tensile strength: 50 MPa
• Flexural modulus: 3000 MPa
• Izod notched impact strength: 5 kJ/m²
• HDT @ 0.45 MPa: 150 °C
• Drying recommendation: 70 °C for 12 hours before use

Tips

Use a hardened steel nozzle to prevent wear from the carbon fiber. Dry the filament at 70 °C for 12 hours before printing to achieve optimal mechanical properties and surface finish.