Polymaker Fiberon PPS-CF10 is a high-performance 3D printing filament based on polyphenylene sulfide (PPS) reinforced with 10% chopped carbon fiber. Its outstanding heat resistance, with a heat deflection temperature of 200 °C at 0.45 MPa, makes it suitable for demanding applications in automotive, aerospace, and industrial environments.

Advantages

The carbon fiber reinforcement provides high stiffness and dimensional stability, while the PPS matrix offers excellent chemical resistance and low moisture sensitivity. The filament prints with low shrinkage, enabling accurate parts with minimal warping.

Suitable for

• Functional prototypes requiring high temperature resistance
• Under-the-hood automotive components
• Chemical-resistant parts and housings
• Jigs and fixtures for demanding environments

Key specifications

• Material: Polyphenylene Sulfide (PPS) with 10% chopped carbon fiber
• Diameter: 1.75 mm
• Net weight: 500 g
• Color: Natural Black
• Nozzle temperature: 300–330 °C
• Bed temperature: 100–120 °C
• Print speed: 30–60 mm/s
• Enclosure recommended
• Hardened steel or ruby nozzle required
• Tensile strength: 100 MPa
• Flexural modulus: 8 GPa
• Density: 1.3 g/cm³
• Spool material: Cardboard

Recommendations

For best results, dry the filament before printing and use a heated chamber to minimize warping. A hardened nozzle is essential due to the abrasive carbon fiber.